常用焊接中英文词语翻译
常用焊接中英文词语翻译
焊接热源weldingheatsource
点热源pointheatsource
线热源linearheatsource
面热源planeheatsource
瞬时集中热源instantaneousconcentrationheatsource
热效率thermalefficiency
热能集中系数coefficientofheatflowconcentration
峰值温度peaktemperature
瞬时冷却速度momentarycoolingrate
冷却时间coolingtime
置换氧化substitutionaryoxydation
扩散氧化diffusibleoxydation
脱氧desoxydation
先期脱氧precedentdesoxydation
扩散脱氧diffusibledesoxydation
沉淀脱氧precipitationdesoxydation
扩散氢diffusiblehydrogen
初始扩散氢initialdiffusiblehydrogen
100℃残余扩散氢diffusiblehydrogenremainedat100℃
残余氢residualhydrogen
去氢dehydrogenation
去氢热处理heattreatmentfordehydrogenation
脱硫desulphurization
脱磷dephosphorization
渗合金alloying
微量合金化microalloying
一次结晶组织primarysolidificationstructure
二次结晶组织secondarysolidificationstructure
联生结晶epitaxialsolidification
焊缝结晶形态solidificationmodeinweld-bead
结晶层状线ripple
多边化边界polygonizationboundary
结晶平均线速度meansolidificationrate
针状铁素体acicularferrite
条状铁素体lathferrite
侧板条铁素体ferriteside-plate
晶界欣素体grainboundaryferrite;polygonalferrite;pro-entectoidferrite
粒状贝氏体granularbainite
板条马氏体lathmartensite
过热组织overheatedstructure
氏组织Widmannst?
ttenstructure
M-A组元martensite-austeniteconstituent
焊件失效分析failureanalysisofweldments
冷裂判据criterionofcoldcracking
冷裂敏感系数coldcrackingsusceptibitycoefficient
脆性温度区间brittletemperaturerange
氢脆hydrogenembrittlement
层状偏析lamellarsegregation
愈合healingeffect
断口金相fractography
密封圈Sealingring
铰链Hinge
把手Handle
平衡块Balanceblock
焊接welding
坡口groove
单面坡口Singlegroove
双面坡口Doublegroove
Ⅰ形坡口Squaregroove
V型坡口Singlevgroove
U型坡口Singleugroove
X形坡口Singlevgroove
K形坡口Singlebevelgroove
12
Y形坡口Singlevgroovewithbroadroodface
坡口面Grooveface
坡口角度Grooveangle
焊缝倾角Weldslope
接头根部Rootofjoint
根部间隙Rootgap
钝边Rootface
焊接接头Weldingjoint
对接接头Buttjoint
角接接头Cornerjoint
T形接头T-joint
搭接接头Lapjoint
十字接头Crossshapedjoint
母材Basemetal(parentmetal)
13
填充金属Fillermetal
热影响区Heat-affectedzone(HAZ)
过热区Overheatedzone
焊合线Bondline(fusionline)
焊接区Weldzone
焊缝区Weldmetalarea
焊缝weld
连续焊缝Continuousweld
断续焊缝Intermittentweld
纵向焊缝Longitudinalweld
横向焊缝Transverseweld
对接焊缝隙Buttweld
角焊缝Filledweld
并列断续角焊缝Chainintermittentfillet
14
交错断续角焊缝Staggeredintermittentfillet
焊缝正面Faceofweld
焊缝背面Backofweld
焊缝宽度Weldwidth
焊缝长度Weldlength
焊缝余高Reinforcement
焊脚Leg(ofafilletweld)
焊脚长度Leglength
套管接头Muffjoint
手工电弧焊Manualarcwelding(shieldedmetalarcwelding)
直流电弧焊Directcurrentarcwelding
交流电弧焊alternatingcurrentarcwelding
弧焊变压器Arcweldingtransformer
15
弧焊整流器Arcweldingrectifier
自动焊Automaticwelding
埋弧自动焊Submergedarcwelding
半自动焊Semi-automaticwelding
氩弧焊Argon-arcwelding
二氧化碳气体保护焊CO2gasshieldedarcwelding
氧乙炔焊Oxy-acetylenewelding
气割Gascutting
碳弧气刨Carbonarcairgouging
水下切割Underwatercutting
等离子弧切割Plasmaarccutting
连续焊Continuouswelding
断续焊Intermittentwelding
点焊Sportwelding
16
对接焊Buttwelding
角焊Filletwelding
搭接焊Lapwelding
返修焊Re-welding
补焊Repairwelding
定位焊Tackwelding
封底焊Backsealingwelding
打底焊Backingwelding
堆焊Surfacing(overlaying)
塞焊Plugwelding
槽焊Slotwelding
盖面焊Consmeticwelding
前倾焊Forwardwelding
后倾焊Backwardwelding
17
分段退焊Backstepwelding
分段多层焊Blockwelding
深溶焊Deeppenetratingwelding
跳焊Skipwelding
质衬垫焊Ceramicbackingwelding
引弧Strikingthearc
焊接工艺参数Weldingcondition
焊接电流Weldingcurrent
焊接电压Weldingvoltage
焊接速度Weldingspeed
电弧电压Arcvoltage
焊丝间距Wirespacing
空载电压Opencircuitvoltage
熔化速度Meltingrate
18
送丝速度Wirefeedrate
气体流量Gasflowrate
焊丝伸出长度Wireextension
极性Polarity
正极/阳极Positiveelectrode
负极/阴极Navigateelectrode
左焊法Leftwardwelding
右焊法Rightwardwelding
电流密度Currentdensity
线能量Heatinput
预热Preheat
后热Post-heat
预热温度Preheattemperature
后热温度Post-heattemperature
19
层间温度Inter-passtemperature
焊后热处理Post-weldheattreatment
锤击Peening
全焊透Fullpenetrationwelding
熔池Weld-pool
熔深Penetration
弧长Arclength
喷射过渡Spraytransfer
短路过渡Shortcircuitingtransfer
熔滴过渡Metaltransfer
焊缝成形Appearanceofweld
焊缝成形系数Formfactorofweld
熔敷系数Depositioncoeffcient
熔敷效率Depositionefficiency
20
熔合比Penetrationratio
等速送丝Constantwire-feedsystem
变速送丝alternatewire-feedsystem
电弧静特性Staticcharacteristicofarc
电弧动特性dynamiccharacteristicofarc
焊接性试验Weldabilitytest
焊接结构Weldedconstruction
焊道Bead
焊层Layer
正接(正极性)Straightpolarity
反接(反极性)Reversedpolarity
焊接位置Posit