常见高分子热膨胀系数CTEWord文档格式.docx
《常见高分子热膨胀系数CTEWord文档格式.docx》由会员分享,可在线阅读,更多相关《常见高分子热膨胀系数CTEWord文档格式.docx(8页珍藏版)》请在冰豆网上搜索。
11.5
6.4
Bismuth
13
7.3
Brass
18.7
Brickmasonry
5.5
3.1
Bronze
18.0
10.0
Cadmium
30
16.8
Calcium
22.3
12.4
Carbon-diamond
1.2
0.67
CastIronGray
10.8
6.0
Celluloseacetate(CA)
72.2
Celluloseacetatebutynate(CAB)
80-95
Cellulosenitrate(CN)
100
55.6
Cement
Cerium
5.2
2.9
Chlorinatedpolyvinylchloride(CPVC)
66.6
37
Chromium
6.2
3.4
Claytilestructure
5.9
3.3
Cobalt
12
6.7
Concrete
14.5
8.0
Concretestructure
9.8
Constantan
18.8
Copper
16.6
9.3
Copper,Beryllium25
17.8
9.9
Corundum,sintered
6.5
3.6
Cupronickel30%
16.2
9
Diamond
1.1
0.6
Dysprosium
Ebonite
76.6
42.8
Epoxy,castingsresins&
compounds,unfilled
55
31
Erbium
12.2
6.8
Ethyleneethylacrylate(EEA)
205
113.9
Ethylenevinylacetate(EVA)
180
Europium
35
19.4
Fluoroethylenepropylene(FEP)
135
75
Gadolinium
5
Germanium
6.1
Glass,hard
Glass,Pyrex
4.0
2.2
Glass,plate
9.0
5.0
Gold
14.2
8.2
Granite
7.9
4.4
Graphite,pure
Hafnium
HardalloyK20
6
HastelloyC
11.3
6.3
Holmium
11.2
Ice
51
28.3
Inconel
12.6
7.0
Indium
33
18.3
Invar
1.5
0.8
Iridium
Iron,pure
12.0
Iron,cast
Iron,forged
Lanthanum
12.1
Lead
28.0
15.1
Limestone
8
Lithium
46
25.6
Lutetium
Magnesium
25
14
Manganese
Marble
5.5-14.1
3.1-7.9
Masonry
4.7-9.0
2.6-5.0
Mica
3
1.7
Molybdenum
2.8
Monel
13.5
7.5
Mortar
7.3-13.5
4.1-7.5
Neodymium
9.6
5.3
Nickel
13.0
7.2
Niobium(Columbium)
7
3.9
Nylon,generalpurpose
72
40
Nylon,Type11,moldingandextrudingcompound
Nylon,Type12,moldingandextrudingcompound
80.5
44.7
Nylon,Type6,cast
85
47.2
Nylon,Type6/6,moldingcompound
80
44.4
Osmium
Palladium
11.8
6.6
Phenolicresinwithoutfillers
Plaster
16.4
9.2
Platinum
Plutonium
54
30.2
Polyallomer
91.5
50.8
Polyamide(PA)
110
61.1
Polybutylene(PB)
Polycarbonate(PC)
70.2
39
Polycarbonate-glassfiber-reinforced
21.5
Polyester
123.5
69
Polyester-glassfiber-reinforced
Polyethylene(PE)
200
111
Polyethylene(PE)-HighMolecularWeight
60
Polyethyleneterephthalate(PET)
59.4
Polyphenylene-glassfiber-reinforced
35.8
20
Polypropylene(PP),unfilled
90.5
50.3
Polypropylene-glassfiber-reinforced
32
18
Polystyrene(PS)
70
38.9
Polysulfone(PSO)
55.8
Polyurethane(PUR),rigid
57.6
Porcelain
2.0
Potassium
83
46.4
Polyvinylchloride(PVC)
50.4
28
Polyvinylidenefluoride(PVDF)
127.8
71
4.5
2.5
46.1
Praseodymium
3.7
Promethium
11
Quartz
0.77-1.4
0.43-0.79
Rhenium
Rhodium
Rubber,hard
77
Ruthenium
9.1
5.1
Samarium
12.7
7.1
Sandstone
11.6
Scandium
10.2
5.7
Selenium
3.8
2.1
Silicon
Silver
19.5
10.7
Slate
Sodium
39.1
Solder50-50
24.0
13.4
Steatite
8.5
Steel
SteelStainlessAustenitic(304)
17.3
SteelStainlessAustenitic(310)
14.4
SteelStainlessAustenitic(316)
16.0
8.9
SteelStainlessFerritic(410)
Strontium
22.5
12.5
Tantalum
Tellurium
36.9
20.5
Terbium
10.3
Terne
Thallium
29.9
Thorium
Thulium
13.3
7.4
Tin
23.4
Titanium
8.6
4.8
Tungsten
4.3
2.4
Uranium
13.9
7.7
Vanadium
VinylEster
16-22
8.7-12
Wood,fir
Wood,oakparalleltograin
4.9
2.7
Wood,oakacrosstograin
Wood,pine
Ytterbium
26.3
14.6
Yttrium
10.6
Zinc
29.7
16.5
Zirconium
3.2
一些液體的體積熱膨脹係數γ
物質
γin10-3/K20°
C
酒精(乙醇)
1.10
丙酮
1.43
汽油
1.06
苯
1.23
氯仿(三氯甲烷)
1.28
果酸
1.07
乙醚
1.62
乙酸乙酯
1.38
甘油(Propantriol)
0.49
甲醇
Mineralol(Hydraulikol)
0.70
石蠟
0.76
煤油
0.96
水銀
0.18
松節油
1.00
四氯化碳
1.22
甲苯
1.12
水
0.21