1、 Q345B:GB/T 1591-94 Type or Grade: Q345B+Q345B Thickness Range: Unlimited Diameter Range: 600mm FILLER MATERIAL AWS A5.20E71T-1 Brand Name: ATYJ502(Q) Diameter: 1.2mm SHIELDINGFlux:Gas:Gas flow:Any Special Backing or Drying:POSITIONPosition of Groove: 2 F Fillet: Yes Vertical Progression(Up or Down)
2、:TECHNIQUEStringer o r Weave Bead: Stringer and Weave Bead Multi-pass or Single Pass(per side): Multi-pass Max. Width of Weave: 18 mm Interpass Cleaning: Wire Brush/Grinding (If necessary) Number of Electrodes: Single PREHEAT Preheat Temp., Min.: Ambient,( 30mm;150) Interpass Temp., Min.:Interpass T
3、emp., Max.: 250 Heating Method: Burner with gas POSTWELD HEAT TREATMENTTemp.:Time:EQUIPMENTType: KR500 WELDING SITE CONDITIONS: In The Shop OTHER:PREPAREDREVIEWEDAUTHORITYWPW No.: W-HL-001WELDING PROCEDUREWeldingprocessWeldpassFillermaterialCurrentVoltsSpeed(cm/min)Energyinput(kj/cm)NameDia.(mm)Type
4、&polarityAmp.FCAWRootATYJ502(Q)1.2DCRP19025022282540-Fill2202802430CapJoint Detail Welding SequenceNote: 1. Cleaning the weld before welding.REVOEWED(WPQR) P-HL-001PQR P-HL-001 According PQR No.: W-HL-001 AWS D1.1-2006 Test Piece Thickness: 16mm+16mm FILLER MATAL AWS A5.20 E71T-1 Ambient 196 PQR No.
5、:InputInterpassTemp()12302532.810.52122402736.210.765337.410.485434.511.397538.910.0124637.5196PQR TEST RESULTS:VISUAL INSPECTION: Acc. Reprot No. VI2009-001RT EXAMINATION: N/A Reprot No. N/A UT EXAMINATION: Acc. Reprot No. N/A MT EXAMINATION N/A Reprot No. UT2009-001TENSILE TESTSpecimenNo.WidthThic
6、knessTensileLoad(KN)Strength(N/mm2)Location of FranctureResultReport-BEND TESTType of bendRollersdiameterAngleIMPACT TESTSize(mm)LocationOf notchType ofnotchTemp.Energy value(Transverse)AverageHARDNESS:(C01) Yes See Report LH2009-001 MACROETCH(C02) Yes See Report LH2009-001 OTHER TEST:Welders Name:
7、Welding date: We, the undersigned, certify that the statement in this record are correct and that the test welds were prepared, welded, and in accordance with the requirements of Rules for AWSD1.1-2006.1.Cleaning the weld before welding.焊接工艺评定外观检验报告WELDING PROCDURE QUALIFICATION VISUCL INSPECTION RE
8、PORT单位名称:安徽鸿路钢结构(集团)股份有限公司 报告号: REPORT NO,:HL-2009-001序号焊接工艺评定编号WPQ NO.焊 工 号 码Welder No.结 果P-HL-001HL-050ACC备注: 经外观检查,焊缝表面无任何缺陷。Remarks: After visual inspection, No any defects in the surface of welds.焊接监督员Welding Supervisor批准Authority日期Date 磁粉检测报告Magnetic powder inspection report项目名称:焊接工艺评定(WPQ)评定号
9、报告编号MT2009-001WPQ NoReport No部件名称试片(Test Piece)执行标准JB/T 4730-2005Part nameAcc. Stand探伤部位-检件材质Q345B+Q345BTest LocationMaterial表面状态打磨检测比例100%评定级别Level 1Surface preparationGrindingTest RateInspection Stand仪器型号B310S电流类型AC检验方法湿磁粉Instrument typeElectric CurrentInspect MethodWet Magnetic particle磁化方式连续法提升力
10、45N磁极间距200mmMagnetizing MethodContinue MethodLifting ForceMagnetic Pole Distance磁化方向交流磁轭磁粉种类Fe3O4悬浮剂水剂Magnetic DirectorAC-YOKEMagnetic ParticleDetecting MediumWater磁化时间2S磁悬液浓度15g/l灵敏度试片A-30/100Magnetizing TimeConcentrationSensitivity Block部件编号焊缝编号检测日期缺陷类型缺陷位置缺陷长度缺陷处理结论Part NoWeld NoTest DateDefect N
11、ameDefect PositionDefect LengthDefect TreatmentJudgeP-001100%角接焊缝2009.6.5-合格检测: 审核: 检测专用章 批准:日期: 日期:硬度检测报告HARDNESS TEST REPORT委托单位OrdererReport No.LH2009-001标准According standardAWS D1 1-2006产品名称Product name焊接工艺认可试验Welding Procedure qualification testPQR号PQR No.试样号Test MarkA01LocMark78910111213-A168171166195213226214223185179205224B201188199215236244216169注:此结果仅对来样负责 Note: Results are responsible for the speci218m235e228n196审查者: 检测者: 批准:Inspector Tester Authority