CETL全球实验室加速循环腐蚀试验

1.0introduction介绍

1.1TESTSCOPE试验范围

Thisstandardspecifiesanacceleratedlaboratoryatmosphericcorrosiontest.Thetestingenvironmentaddressedissimilarineffecttothatofthesaltload/climaticpartoftheprovinggroundcorrosiontestprocedure,CETP00.00-R-343andyieldscorrespondingresults.Theobjectiveofthetestistoallowevaluationofthecorrosionresistanceofmetalsinenvironmentswherethereisasignificantinfluenceofchlorideions,mainlyassodiumchloridefromamarinesourceorbywinterroadde-icingsalt.Thelaboratorytestprovidesfullexposuretothesaltloadandhumidityenvironment.Itdoesnotattempttosimulateotherengravingfactorssuchasmudloads,temperaturestressesorwear.Itservesasageneralpurposeatmosphericcorrosiontestandappliestoavarietyofmaterials,coatings,andinteractionsofmaterials,bothastestspecimensorindesignedcomponents.Thetestcanbeusedasadesignverificationmethodinorderto（a）developandqualifynewcorrosionresistantproducts,（b）developnewpre-treatmentsandfinishingprocesses,（c）selectmaterialsand,（d）performqualitycontrolofthefinalproduct.

本标准是关于一项在实验室里加速进行的大气腐蚀试验。

本文所述的试验环境类似于《试验场腐蚀试验程序CETP00.00-R-343》中的盐负荷/环境影响部分，得出相应的结果。

试验目的在于评估金属在富含氯化物的环境中（主要是海水中的盐或冬天用于融雪的盐）的抗腐蚀性。

该实验室试验主要是将试验件完全暴露在湿润的盐负荷环境中，而非模拟其他摩擦因素如泥负荷、温度压力或磨损。

该试验主要作为一项大气腐蚀试验，适用于各种各样的材料、涂层、试样或设计零部件材料的相互作用。

该试验可作为一种验证设计的方法，用于（a）开发并验证新的抗腐蚀产品；（b）开发新的预处理和表面处理工艺；（c）选择材料；（d）对最终产品的质量控制。

Thestandardspecifiescontrolledconditionsforequipmentandprocedurestoallowthetesttobeperformedwithahighdegreeofrepeatabilityandreproducibility.Itisdesignedtobesuitabletoruninvariousclimatechambers,eitherasafullyautomatedprocedureorwithpartialmanualoperations.

本标准说明了设备和程序的受控条件，让实验具有高度的重复性和再现性。

本标准适用于多种环境试验箱，包括全自动试验或部分手动操作的试验。

1.2SUMMARYOFTESTCONTENT试验内容摘要

Theworkdaytestprocedureconsistsof:

工作日的试验程序由以下几个方面组成：

∙A6hwetphaseatroomtemperature.withintermittentexposuretosaltsolution（0.5%NaCl）.

∙A2.5htransitionphasewithdryingunderclimatecontrol.

∙A15.5hphasewithconstanttemperatureandhumidity（50?

C,70%RH）.

∙室温下6小时的加湿阶段，间歇曝露到0.5%的氯化钠溶液中

∙2.5小时的过渡阶段，通过环境控制进行烘干

∙15.5小时的恒温恒湿阶段（50?

C,70%RH）

AfterrepeatingthisprocedureMon-Fria48hweekendphaseundercontinuedconstantclimatecontrolisadded.

从周一到周五重复该试验程序后，在周末加入持续恒定环境控，进行48小时的试验。

1.3COMMONALITY共通性

ThisisaCONTROLTESTandcanbeusedtoqualifycomponentsthroughouttheworld.Thetestmaybeconductedatanylocationhavingthenecessaryequipmentandfacilities.ProposedrevisionstothisproceduremustbesubmittedperFAP03-179.

这是一项可验证世界上所有的零部件的控制试验，可在任何地方进行，只要具备所需的设备仪器。

对本试验程序的修改建议必须按FAP03-179提交。

2.0Instrumentation仪器

Thefollowingelementsareusuallyrequiredtoconductthetestprocedure:

进行试验程序一般需要以下仪器：

2.1Compressed,cleanairof4-6barsforcleaningsaltsolutionfromspraynozzles,asasourcefortherenewalofchamberairandforhumidification,suppliedbysprayhumidifiers.

2.14-6bar的干净的压缩空气，用于清理喷嘴上的盐溶液、箱内换气和喷雾加湿器进行加湿。

2.2Alowconductivitywatersupply（20?

Smax）forhumidificationorevaporativesprayhumidifiersandforthepreparationofsaltsolutions.

2.2一根低导电率的供水管（最大20?

S），用于加湿或喷雾加湿器以及准备盐溶液。

2.3Atankforpreparationandstorageofsaltsolutionor,alternatively,asystemfordirecton-linemixingofwaterandsaturatedNaClsolutiontotheactualconcentration（0.5?

0.05%byweight）

2.3一个用于准备和存储盐溶液的水槽，或者一套直接在线按实际浓度（0.5?

0.05%，按重量）混合水和饱和氯化钠溶液的系统。

2.4Aconductivitymeterwithbuilt-intemperaturecompensationforpreparationandcontrolofthe0.5%NaClsaltsolution（conductivity:

8.3mS/cm+0.80at20?

C）.A0.50%byweightNaClsolutionisusedasacalibrationstandardateachmeasurement.

2.4一个带内置温度补偿的电导仪，用于准备和控制0.5%的氯化钠盐溶液（温度为20?

C时的导电性：

8.3mS/cm+0.80）。

一份按重量为0.50%的氯化钠溶液，作为每次测量时的校正标准。

2.5Ahighqualitydeviceforindependentcontroloftemperatureandrelativehumidityshallbeaccessible.Thisinstrumentshallonastipulatedregularinterval（Ref5.4）beusedforindependentmonitoringandcalibrationoftheconditionsintheverytestplaneoftheexposurechamber.Thetotalmeasurementerrormustnotexceed0.1?

C.

2.5一套高质量的设备，用于独立控制温度和相对湿度。

该设备按照规定的时间间隔（参考5.4），独立监控和校正试验箱李的试验平面上的各项条件，测量总误差不超过0.1?

C。

2.6Racksofinertmaterialforsupportandalignedfixationoftestspecimensmustnothamperafreeair-flowaroundthetestobjects,norcollectstandingwetness.Thetestobjectsinarackmustnotscreenoneanotherfromthesaltsolutiondownfallandtheyshouldbeexposedwiththestipulatedexposureangletothespray（15-20degreesinclinationfromvertical）.

2.6由惰性材料制成的夹具，用于支撑、排列和固定试样，但不得妨碍试样周围的空气流通，不得累积水分。

夹具上的试样不得相互遮蔽导致盐溶液淋不到试样上。

试样应按规定的角度曝露到喷雾中（偏离垂直线15-20度）。

2.7Pressurizedhand-sprayequipmentforapplicationofthe0.5%NaClsolution

2.7如需采取手动喷洒，应使用适用于0.5%盐溶液的加压型手动喷雾器，喷雾器的容量必须能

2.8Funnels,beakers/measuringglassesandabalancewithatleast0.1gaccuracyformonitoringandcalibrationofsaltsolutiondownfallthroughoutthetestplaneoftheexposurechamber.

2.8漏斗、烧杯/量杯以及精确度至少为0.1g的天平，用于监控和校准曝露箱中试验平面上落下的盐溶液。

2.9AlltestmeasurementequipmentmustbecalibratedandmaintainedperFAP03-015,Control,Calibration,andMaintenanceofMeasurementandTestEquipment.

2.9所有试验的测量设备的校准和维护必须按照《FAP03-015测量和试验设备的控制，校准和维护程序》。

2.10Allapplicablesafetyguidelinesandproceduresmustbefollowed.

2.10试验须遵守所有适用的安全指引和安全程序。

3.0Equipmentandfacilities设备设施

Thenecessary,permanentlyinstalledfacilitytoconductthetestconsistsofaprogrammablehumiditychamberofgoodquality.Itispreferablyequippedwithanintegratedrigforsprayingsaltsolutionoftherequiredamountandaccuracy,coolingcapacityandagoodinternalcirculationsystemfortheconditionedair（Fig.1）.Theexposurechambershallbedesignedsothatthetestconditionsdescribedinthesubsequentparagraphscanbeobtained,controlled,andmonitoredduringthetest.

试验所需的永久性安装的设施包括一个可编程的高质量湿度箱。

湿度箱中最好能配备一套喷量准确度高的综合性盐雾喷洒装置、冷却装置和一套性能良好的空气内循环系统（如图1）。

曝露箱应按要求设计，以使下文所述的试验过程中的各项条件能在得到满足、控制和监控。

Fig.1Schematicviewofaclimatechamberequippedwithfunctionssuitedforperformanceofthedescribedtestprocedure:

1.Chambertestspace,2.Climatizationunit,includingfan,heating,coolingandhumidification,3.Testplanewithsamples,4.Temperature/humiditysensorforregulation,5.Insulatedwalls/lids,6.Diffusorsforimprovedairdistribution,7.Freshairinlet/"bleed",8.Rainrigwithnozzlesandmotorforswayingmode,9.Gutter,10.Control/steering/recordingunit,11.Positionformonitoring/calibrationofclimatewithindependenttemperature/humiditysensor.

图1环境试验箱的图示，配备了进行本文所述的试验程序所需的功能：

1.试验空间；2.环境系统，包括风扇、加热器、冷却器和加湿器；3.放置试样的平面；4.温湿传感器（调节用）；5.隔热壁/盖；6.空气扩散器（改善空气分布）；7.新鲜空气进气口；8.带喷头和摇摆模式驱动马达的喷洒器；9.排水口；10.控制/操作/记录系统；11.带独立温室感应器的环境监控/校正位置。

3.1CLIMATECONTROL环境控制

Thehumidityandtemperaturelevelsofthechamberduringthetestcycleshallbecontinuouslymonitored.Thesensorsshouldreflecttheclimateconditionsinthetest"plane"（Fig.1,item4）.Themeanvalueoftheconstanttemperature/relativehumidityclimateconditionsmustbewithin±0.4?

Cand?

2%relativehumidity（RH）respectivelyvs.thereal,setvalue,i.e.thesearethemaxtolerablemeanoffsetscausedbythesumofcalibrationerrors.Atannualcalibrationthisdegreeofaccuracymustbefulfilledforthefollowingthreeconstantconditions:

25?

C,95%RH,50?

C,95%RHand50?

C,70%RH.Atbimonthlycontrol,duringnormaloperation,thisaccuracyshouldbefulfilledattheconstantclimateconditions（50?

C,70%RH）duringawork-daycycle.

试验过程中应连续不断地监控试验箱的湿度和温度水平。

传感器会反映试验“平面”上的环境（如图1中第4项）。

恒定温度/相对湿度的均值必须在±0.4?

C范围内，相对湿度（RH）在±2%，分别对应实际值、设定值，这些就是由于累积的校正误差造成的平均偏移值的最大允许范围。

在年度校正过程中，这一精确度必须得到满足，以保证以下三项恒定条件：

25?

C,95%RH,50?

C,95%RH以及50?

C,70%RH。

在进行两月一次的正常控制时，工作日循环中的恒定环境条件（50?

C,70%RH）应能到达这一精度。

Themaximumallowedshort-termfluctuationsinrelativehumidityoverlaidonthecalibratedmeanvalueis?

3%RH,whichimpliesamaximumallowedshort-termtemperaturefluctuationof±0.6?

C.Figure2isexemplifyingtherequirementonrelativehumidity.

叠加到校正平均值的相对湿度短期波动最大范围是?

3%RH。

这意味着短期温度波动的最大范围只能是±0.6?

C。

图2举例说明了相对湿度的要求。

SetRHvalue

相对湿度设定值

Fig.2Accuracyrequirementonhumiditydeviationsfromsetvalue

图2湿度偏差离设定值的精确度要求

Thechambercontrollingsoftware/hardwaremustbedesignedsothattherelativehumiditymaybechangedlinearlywithtimeasdepictedintheillustratedtestconditions,seeFigure5.Inthe2-stagerampingfromawetchamberat25±2?

Ctohumidconditionsat50?

C,70%RH,thefirstheatingstageto40?

Cshouldbereachedwithin30minuteswithoutsampledrying,whichissecuredbyanominalrelativehumiditysettingto95%RH.Thesecond2hrampmustreachthestipulatedfinal50?

C,70%RHattheendoftheramp.

控制试验箱的软件/硬件必须设计成能使相对湿度随时间呈线性变化，如图5所示。

从试验箱温度为25±2?

C的湿润状态到50?

C,70%RH的湿润状态需经过两个阶段。

第一阶段应通过将相对湿度读数设定到95%RH，以保证温度在30分钟内达到40?

C而试样不干燥。

第二阶段为两小时，必须在结束前达到规定的50?

C,70%RH。

NOTE:

Foreachnewexposuresituationthisconditionmustbeverifiedbyanindependentmonitoringdevice（paragraph2.5）withthesensorpositionedamongtheactualtestobjectsintheiractualaverageplaneofexposure（Fig.1Item11）.Formonitoring:

Deploythesensordirectlyafterthelastsprayeventofthework-daywetphase.

注意：

每次曝露的条件必须经过独立监控设备验证（见第2.5段），也就是实际试验物体所在的曝露平面之间的传感器（如图1，第11项）。

在工作日湿润阶段的最后一次喷洒后直接调节传感器来进行监控。

Inautomatedtesting,forcedcoolingisnecessarywhenproceedingfrom50?

C,70%RHcontrolled,constantconditionstomacro-wetconditionsat25?

C.Thechambermustachieveacoolingfrom50?

Cto30?

Cwithin30minuteswiththetargeted25?

Cmetwithin1hour.Ifsprayingisappliedmanually,thencoolingthesamplesbylettingthechamberbeopenwithtestobjectskeptwetmayprovid