球铁配料计算_.xls

球铁配料计算_.xls

《球铁配料计算_.xls》由会员分享，可在线阅读，更多相关《球铁配料计算_.xls（2页珍藏版）》请在冰豆网上搜索。

球铁配料计算本本列列配配料料单单名称化学成份（%）加入量（%）熔化量（Kg）CSiMnCrNiMoCuPSMgRE输入列1000生铁4.410.20.070.140400废钢0.250.30.610.040.0453.67536.7增碳剂1002.3323.3回炉料3.72.70.4150.040.0200铁料合计4.2240.5610.40700000.0490.061000收得率%97958575100100100100100000铁水合计4.0970.5330.34600000.0490.061000硅铁0.2750.40.040.021.313锰铁72.5650.20.0300钼铁00铬铁00镍00铜00合金合计0.0030.9750.00500005E-043E-040收得率%10010080751001001001001000收得合计0.0030.9750.00400005E-043E-040铁水成份4.11.5080.3500000.050.062000球化剂404731.717孕育剂0.2650.40.040.02110球孕合计0.0021.330.0724E-042E-040.1190.0510收得率%10010010010042800收得合计0.0021.330.07200004E-0400.049980.04080球铁成份3.9022.8380.42200000.050.0620.049980.04080退火铁素体3.5-3.92.0-2.70.60.070.020.03-0.060.02-0.04CE铸态铁素体3.5-3.92.5-3.00.30.070.020.03-0.060.02-0.044.84803625低温铁素体3.5-3.91.4-2.00.20.040.010.04-0.06铸态珠光体3.6-3.82.1-2.50.3-0.50-0.20.5-1.00.070.020.03-0.060.02-0.04热处理珠光体3.5-3.72.0-2.40.4-0.80-0.20-1.00.070.020.03-0.060.02-0.042.3-2.3铸态组织中珠光体为主2.5-2.9铸态组织中铁素体大于珠光体3.2-4.0铸态组织基本为铁素体使用方法：

1.在炉料行输入各种炉料的化学成份。

2.收得率行输入各种元素收得率。

如果不清楚，就用现生产的品种核算一下。

3.在加入量（%）输入列中输入各种炉料加入百分比,废钢一项不能输入。

4.看铁水成份和球铁成份两行是否附合工艺要求，如不附合则修改加入量输入列中炉料加入百分比，直到附合工艺要求。

5.输入熔化量，则得到配料单。

6.千万注意表中红色字不能改动，易碎！

将文件多作个备份。