高温合金材料牌号及化学成分Word文档下载推荐.doc
《高温合金材料牌号及化学成分Word文档下载推荐.doc》由会员分享,可在线阅读,更多相关《高温合金材料牌号及化学成分Word文档下载推荐.doc(5页珍藏版)》请在冰豆网上搜索。
≤0.04
2
ZG50Cr28Ni6
0.45~0.55
≤1.50
4.0~7.0
3
ZG35Cr24Ni7SiN
0.30~0.40
1.30~2.00
0.8~1.5
23.0~25.5
7.0~8.5
≤0.03
N:
0.2~0.28
4
ZG35Cr28Ni10
8.0~11.0
5
ZG30Cr26Ni12
24.0~28.0
11.0~14.0
6
ZG33Cr25Ni14
0.28~0.38
12.0~14.0
7
ZG35Cr28Ni16
14.0~18.0
8
ZG30Cr25Ni20
23.0~27.0
19.0~22.0
9
ZG40Cr25Ni20
0.35~0.45
10
ZG40Cr25Ni20Si2
1.40~2.00
≤2.0
18.0~22.0
11
ZG45Cr24Ni24NbTi
0.40~0.50
≤1.0
22.0~25.0
0.7~1.5
Ti:
0.1~0.5
12
ZG30Cr30Ni20
28.0~32.0
8.0~22.0
13
ZG40Cr30Ni20
14
ZG40Ni25Cr21
19.0~23.0
15
ZG14Ni32Cr20Nb
0.10~0.18
≤1.25
30.0~35.0
16
ZG40Ni35Cr25
≤2.00
33.0~37.0
17
ZG40Ni35Cr25Nb
24.0~27.0
32.0~37.0
0.6~1.5
18
ZG40Ni35Cr25NbW
1.0~2.0
19
ZG50Ni35Cr17
0.40~0.60
15.0~19.0
20
ZG50Ni39Cr19
17.0~21.0
37.0~41.0
21
ZG45Ni48Cr28W5Si2
26.5~29.5
47.0~50.0
4.0~6.0
22
ZG40Ni48Cr30W15Si2
1.0~1.5
45.0~50.0
14.0~17.0
23
ZG50Ni36Cr26Co15W5
0.75~1.6
0.1~0.7
34.0~38.0
≤0.035
Co:
13.0~17.0
24
ZG42Ni33Cr25Nb
0.40~0.45
32.0~35.0
1.0~1.8
Ti+Zr(微量)
25
ZG45Ni35Cr27NbW
≤0.6
34.0~37.0
0.3~0.8
0.5~1.5
Nb+W+Mo≤3.0
26
ZG50Ni48Cr18W5
≤1.75
≤1.5
27.0~30.0
27
ZG10Ni32Cr20Nb
0.08~0.16
31.0~34.0
28
ZG45Ni48Cr28W5Co5
1.25~1.75
47.5~50.5
4.0~5.0
4.0~6.0
29
ZG35Ni24Cr18Si2
1.5~2.5
17.0~20.0
23.0~26.0
30
ZG30Ni35Cr15
≤2.5
13.0~17.0
31
ZG45Ni35Cr25NbM
32
ZG40Ni35Cr25W4
0.30~0.50
≤1.8
33
ZG35Cr24Ni7SiN(Re)
1.3~2.0
0.2~0.28
34
ZG10Ni35Cr25Nb
≤1.3
Re:
0.2~0.3
(加入量)
35
ZG50Ni45Cr35NbM
0.4~0.6
43.0~47.0
注:
1、序号6、7钢种制造应确保最少的铁素含量。
2、乙烯列接管Si含量由买卖双方确定。
3.Sn、pb、Zn含量均不超过100PPm
常温力学性能
屈服强度ReL≥MPa
抗拉强度Rm≥MPa
延伸率A≥%
345
560
340
540
275
490
235
245
440
431
441
450
390
186
448
221
242
392
295
315
480
250
265
3.5
195
ZG50Ni45Cr35NbM
高温短时力学性能
760℃
871℃
982℃
1050℃
抗拉强度,
Rm≥MPa
延伸率,