Method to upgrade titania slag and resulting productUGS.docx

1、Method to upgrade titania slag and resulting productUGSMethod to upgrade titania slag and resulting product United States Patent 5,830,420 Borowiec , et al. November 3, 1998 AbstractA method is disclosed including: (a) sizing a titania slag to a particle size range of from 75 microns to 850 microns;

2、 (b) oxidizing the sized titania slag by contacting the sized titania slag with an oxygen containing gas at a temperature of at least about 950.degree. C. for a period of at least about 20 minutes such that a substantial portion of the iron oxide is converted to a ferric state, such that the reduced

3、 titanium oxides are converted to a tetravalent state, and such that at least a major portion of the glassy silicate phase is decomposed; (c) reducing the oxidized titania slag in a reducing atmosphere at a temperature of at least about 700.degree. C. for a period of at least about 30 minutes such t

4、hat the ferric state iron oxide is converted to a ferrous state; (d) leaching the reduced titania slag with mineral acid at a temperature of at least 125.degree. C. and under a pressure in excess of atmospheric pressure to yield an upgraded leached slag product and a leachate; and (e) washing and ca

5、lcining the upgraded leached slag product by heating at a temperature in the range of from 600.degree. C. to 800.degree. C. The method provides advantages in that it can be used to produce a product with high TiO.sub.2 content that is suitable for the chloride process of TiO.sub.2 pigment production

6、. Inventors: Borowiec; Krzysztof (Tracy, CA); Grau; Alfonso E. (St-Bruno, CA); Gueguin; Michel (Tracy, CA); Turgeon; Jean-Fran.cedilla.ois (Tracy, CA) Assignee: QIT-Fer et Titane Inc. (Quebec, CA) Appl. No.: 561602Filed: November 21, 1995Current U.S. Class:423/69; 423/74; 423/82; 423/86 Internl Clas

7、s: C01G023/00; C22B034/10Field of Search: 423/86,82,74,69 References Cited Referenced ByU.S. Patent Documents2961298Nov., 1960Tikkanen423/86. 3060002Oct., 1962Leddy et al. 3291599Dec., 1966Reeves. 3457037Jul., 1969Aramendia et al.423/86. 3868441Feb., 1975Agee et al.423/82. 3875286Apr., 1975Robinson

8、et al.423/86. 3897537Jul., 1975Robinson et al.423/86. 3922164Nov., 1975Reid et al.423/86. 4038364Jul., 1977Lailach423/86. 4097574Jun., 1978Auger et al.423/86. 4120694Oct., 1978Elger et al.423/82. 4199552Apr., 1980Rado423/86. 4933153Jun., 1990Gueguin423/82. 5011666Apr., 1991Chao et al.423/82. 5063032

9、Nov., 1991Gueguin423/82. 5389355Feb., 1995Gueguin423/82. Foreign Patent Documents247110Sep., 1963AU. 69483/74Oct., 1976AU. 26 109/77Dec., 1978AU. 767560Sep., 1967CA423/86. 2038191Feb., 1971DE. 2038248Feb., 1971DE. 2425394Dec., 1974DE423/82. 70/5322Jul., 1970ZA. 77/3543Jun., 1977ZA. 94/3488May., 1994

10、ZA. 1092034Nov., 1967GB. 1225826Mar., 1971GB. 1282506Jul., 1972GB423/82. 1477840Jun., 1977GB423/86. WO 94/04709Mar., 1994WO. Primary Examiner: Bos; Steven Attorney, Agent or Firm: Nilles & Nilles ClaimsWhat is claimed is: 1. A method to upgrade a titania slag to obtain a high TiO.sub.2 -containing p

11、roduct having residual impurity content and grain size distribution suitable for use as a feedstock in a chloride process of titanium dioxide pigment production, said titania slag containing reduced titanium oxides and impurities including at least one member selected from the group consisting of ir

12、on oxide, manganese oxide, chromium oxide, vanadium oxide, aluminum oxide, silicon oxide and alkaline-earth oxides, said at least one member being distributed in a pseudo-brookite phase and a glassy silicate phase, the method comprising: (a) sizing the titania slag to a particle size range of from 7

13、5 microns to 850 microns; (b) oxidizing the sized titania slag by contacting the sized titania slag with an oxygen containing gas at a temperature of at least about 950.degree. C. for a period of at least about 20 minutes such that a portion of the iron oxide is converted to a ferric state, such tha

14、t reduced titanium oxides are converted to a tetravalent state, and such that at least a major portion of a glassy silicate phase is decomposed; (c) reducing the oxidized titania slag in a reducing atmosphere at a temperature of at least about 700.degree. C. for a period of at least about 30 minutes

15、 such that the ferric state iron oxide is converted to a ferrous state; (d) leaching the reduced titania slag with mineral acid at a temperature of at least 125.degree. C. and under a pressure in excess of atmospheric pressure to yield an upgraded leached slag product and a leachate; and (e) washing

16、 and calcining the upgraded leached slag product by heating at a temperature in the range of from 600.degree. C. to 800.degree. C. 2. The method of claim 1 wherein the resulting upgraded slag product contains at least 90% by weight of titanium dioxide and less than 1% by weight of magnesium oxide an

17、d less than 0.2% by weight of calcium oxide. 3. The method of claim 1 wherein the alkaline-earth oxide impurities contained in the titania slag comprise magnesium oxide and calcium oxide. 4. The method of claim 2 or 3 wherein the titania slag contains at least 3% by weight of iron oxides. 5. The met

18、hod of claim 4 wherein said titania slag contains at least 1% by weight of magnesium oxide and at least 0.2% by weight of calcium oxide. 6. The method of claim 1 wherein prior to step (b), the titania slag is preheated to improve performance of step (b) and step (b) is conducted in a fluidized bed r

19、eactor. 7. The method of claim 1 wherein step (b) is conducted in a fluidized bed. 8. The method of claim 7 wherein step (b) is conducted at a temperature range of from about 1000.degree. C. to 1100.degree. C. 9. The method of claim 7 wherein step (b) is conducted for a period of between 1 and 2 hou

20、rs. 10. The method of claim 7 wherein a fluidizing gas contains in excess of 2% oxygen. 11. The method of claim 1 wherein step (c) is conducted using a reducing agent that includes at least one member selected from the group consisting of carbon monoxide, hydrogen gas, smelter gas, reformed natural

21、gas and coal. 12. The method of claim 11 wherein step (c) is conducted in a fluidized bed reactor at a temperature range of from about 700.degree. to 900.degree. C. 13. The method of claim 12 wherein step (c) is conducted at a temperature range of about 800.degree. to 850.degree. C. 14. The method o

22、f claim 13 wherein step (c) is conducted for a period of about 11/2 to 2 hours. 15. The method of claim 1 wherein step (d) is conducted at a temperature range of 140.degree. to 160.degree. C., under agitation and at a pressure of at least about 50 psi. 16. The method of claim 15 wherein step (d) is

23、a multiple stage leaching operation. 17. The method of claim 1 wherein said mineral acid includes at least one acid selected from the group consisting of sulfuric acid and hydrochloric acid. 18. The method of claim 17 wherein step (d) is a single stage leaching operation. 19. The method of claim 17

24、wherein step (d) is a two stage leaching operation. 20. The method of claim 17 wherein the mineral acid is present in at least a 10% stoichiometric excess of what is needed to convert leachable oxides and alkaline-earth impurities to soluble chlorides. 21. The method of claim 20 wherein the concentr

25、ation of mineral acid is at least about 15% by weight and step (d) is conducted at a pressure of at least 40 psig. 22. The method of claim 21 wherein the concentration of mineral acid is about 20% by weight and step (d) is conducted at a pressure of from 50 psig to 70 psig. 23. The method of claim 1

26、 wherein step (e) comprises the sequential steps of separating the upgraded leached slag product from the leachate, washing the upgraded leached slag product with water, drying the upgraded leached slag product and then calcining said upgraded leached slag product. 24. The method of claim 15 wherein

27、 the leaching is conducted at a temperature of about 150.degree. C. 25. The method of claim 24 wherein the reduced titania slag is contacted with the mineral acid for a time of 3 to 7 hours. 26. The method of claim 1 conducted in continuous mode as a continuous process. 27. The method of claim 1 con

28、ducted in batch mode. 28. The method of claim 1 wherein step (e) includes a caustic leaching of the upgraded leached slag product that is conducted after said washing and prior to said calcining. 29. The method of claim 28 wherein said caustic leaching is conducted under agitation and in batch mode.

29、 30. The method of claim 28 wherein said caustic leaching is conducted under agitation in continuous mode. 31. The method of claim 29 wherein said caustic leaching is performed with a sodium hydroxide solution at a temperature of at least about 50.degree. C. 32. The method of claim 30 wherein said c

30、austic leaching is performed with a sodium hydroxide solution at a temperature of at least about 50.degree. C. 33. A method of treating a titania slag to obtain an intermediate product including rutile, pseudo-brookite and ilmenite, said titania slag containing reduced titanium oxides and impurities

31、 including at least one member selected from the group consisting of iron oxide, manganese oxide, chromium oxide, vanadium oxide, aluminum oxide, silicon oxide and alkaline-earth oxides, said at least one member being distributed in a pseudo-brookite phase and a classy silicate phase, the method comprising: (a) sizing the titania slag to a particle size range of from 75 microns to 850 microns; (b) oxidizing the sized titania slag by contacting the sized titania slag with an oxygen containing gas