1、13步骤 4 结果14步骤 5: 优化多级螺杆转速和背压曲线15步骤 5 结果16步骤 6: 优化松退17步骤 6 结果18步骤 7: 优化保压曲线19步骤 7 结果20TABULATED RESULTS21步骤 8: 优化锁模力22步骤 8 结果步骤 9: 设定注射压力23步骤 9 结果典型工艺参数公差设定24成型周期分析采用下面表格估计注塑过程中的每一阶段对周期的影响. 然后去机床看正在运行的模具, 写下实际的时间并计算出百分比.哪一阶段在整个周期中占最多的时间 那里可以是最有效的缩短成型周期 模具 1估计 %实际实际%评价 合模射台前进和后退注射时间保压时间冷却时间开模顶出整个成型周期1

2、00%seconds 模具 2评价射台前进和后退 工艺参数优化目标: 一步步改进工艺过程稳定性. 评估各个参数的更改对工艺过程稳定性的影响 to demonstrate the cumulative improvemnt in the process and product consistency 方法:At each stage, after the process has been given sufficient time to stabilise, a run of sixteen consecutive mouldings is to be made. These mouldings

3、 will be assessed for consistency by weight （a dimension, a physical property or some other attribute could equally well be used, weight is simply the most widely applicable）.稳定性通过计算重量的标准偏差来衡量. 同时打印出机床IBED上的过程统计数据. 1.找出转压点2.找出浇口冷却时间3.优化注射速度4.采用正确的螺杆转速5.优化多级预塑曲线6.优化松推7.优化多级保压曲线8.优化锁模力9.设定注射压力限定步骤 1 找

4、出转压点在没有保压压力和保压时间的基础上填满产品95% -98%, 然后设定一定的保压和保压时间生产16模. 初始设置时的指导1采用行程切换2设定切换位置为10-12mm （逐步增加预塑量直到产品打满95% - 98% 的位置） 设置注射压力为最大值4设定保压压力和保压时间均为05设定注射速度 60 mm s-1 设定松推速度为最大值设定锁模力为最大值选择适当的螺杆转速根据材料物性表, 设定料桶温度配置过程统计控制设定保压压力和保压时间生产完整的产品称12 模产品的重量, 计算标准偏差打印:页面 20 工艺参数优化页面 50 工艺过程统计步骤 1 结果输入实际值平均值范围最小最大没保压时的重量

5、有保压后的重量填充的百分比%标准偏差 （16 模）g料垫 （平均值和范围）预塑时间 （平均值和范围）螺杆停止位置 （平均值和范围）注射时间 （平均值和范围）注射压力峰值, P inj. max转压压力, PN press.转压位置 步骤 2 找出浇口冷凝时间设定保压压力为步骤1 上找出的注射压力峰值的50% 左右. 设定保压时间为 1 s .生产数模产品使过程稳定后连续取5模产品称出每模重量和平均值 增加保压时间至2 s, 生产数模产品使过程稳定后连续取5模产品称出每模重量.在保压时间3s, 4s 5s . . . 时重复上述过程直到产品重量不再增加 作出产品重量和保压时间的关系图. 记录Re

6、cord the TCU setting and the actual mould temperature.页面 30 温度XL Spreadsheet graph为什么记录模具温度很重要还有什么因素会影响浇口冷凝时间TCU settingFH temperatureMH temperature C重量 1重量2重量3重量4重量5平均重量时间保压重量1所需的保压时间s步骤 3 优化注射速度采用多级注射曲线, 使注射行程最后的10-20% 采用逐步降低的注射速度. 每次更改注射速度, 必须重新建立转压点. （注意每次保压和保压时间都设定为0.）连续取16模, 计算出标准偏差. 页面 24 MWE

7、 使用和没使用多级保压时的曲线页面 26 多级注射页面50 工艺过程统计为什么转压点要更改注射压力发生了什么为什么在数社的末端采用逐步降低的注射速度是有用的没有保压时的重量采用保压的重量填充百分比螺杆停止位置（平均值和范围）转换位置 步骤 4 采用正确的螺杆转速Select the correct, optimum screw speed for the material being processed （see notes, Section 5 ）. Use this single speed for the whole plasticising strokeSet a back press

8、ure of 5 to 10 bar （hydraulic）.Readjust dosing stroke to achieve 95-98% fillTake sixteeen consecutive mouldings and determine the standard deviation of the weights.Print out:Page 50 Process Statistics Why is it important to use the manufacturers recommended screw speedSTEP FOUR RESULTSInsert actual

9、values in the relevant boxesMean valueRangeminmaxWeight without holding pressureWeight with holding pressurePercentage fillStandard deviation （16 shots）Melt cushion （mean and range）Dosing time （mean and range）Screw stop position （mean and range）Injection time （mean and range）Peak injection pressure,

10、 P inj. maxInjection pressure at changeover, PN press.Changeover stroke STEP FIVEOptimise screw speed and back-pressure profileUse the Dosing Profile page to slow down the screw rotation speed for the last 10% of the metering stroke.Page 21 Dosing ProfilesPage 50 Process StatisticsWhat has happened

11、to the Dosing Stop positionSTEP FIVE RESULTSSTEP SIXOptimise decompressionFind the decompression speed which gives best screw stroke and melt cushion consistency. Set a decompression stroke of 5mm.Check that you still achieve 95-98% fill.What has happened to the screw stop positionWhat is happening

12、to the check ringSTEP SIX RESULTSSTEP SEVENOptimise holding pressure profileUse the Holding Profile page to set a holding pressure profile which ensures a smooth transition from injection to the holding pressure phase and use a high enough pressure to pack the part properly.Add a step which reduces

13、holding pressure gradually to zero.Page 24 MWEPage 27 Holding ProfileWhy do you need a smooth transition from injection to holding pressureWhy bother to reduce the pressure gradually if the gate has already frozenSTEP SEVEN RESULTSTABULATED RESULTS The range value, R, is the maximum minus the minumu

14、m, taken from the seven steps.meanRMelt cushionDosing timeScrew end positionInjection timeInjection pressure P hyd maxInection pressure PN hydraulicChangeover strokeCan you see a trendWhich step had the greatest effect on the consistency of the mouldingSTEP EIGHTOptimising the clamp forceReduce the

15、clamp force by steps of 50 kN （100 kN for machines over 100 tonnes） using the settings far optimised in the seven steps above.Allow the process to stabilise each time and then weigh five mouldings.Tabulate your results below and plot a graph of tonnage against part weight.Does the mould require the

16、expected clamp forceWhat are the advantages of running at reduced tonnageSTEP EIGHT RESULTSEnter results in XL spreadsheet. Print out graph.Weight 1Weight 2Weight 3Weight 4Weight 5Mean weightClamp forceRequired clamp forcekNSTEP NINESet injection pressureUntil now the injection pressure has been set

17、 to the machines maximum value. From the Process Statistcs page it can be seen that the machine does not need all that pressure to fill the mould.Gradually decrease the set injection pressure until the injection time starts to increase. Increase the pressure again until the previous injection time i

18、s established with a consistency of s or better preferably to s variation.What is the purpose of limiting the injection pressureSTEP NINE RESULTSActual peak injection pressurebarAppendix 1TYPICAL PROCESS TOLERANCESShot-weight deviationPlasticising timeCycle time % 1%Screw position, dosing stopMelt temperature 2C 3 5Mould temperature 1 4Barrel tem